 | | | | Maxxon Level-Right |
| | | | Material: Hydraulic cement |
| | | | Dry Density: Approximately 125 pcf (2003 kg/cu.m) |
| | | | Compressive Strength, per modified ASTM C 109, at 28 days: 5500 psi (38 MPa). |
| | | | Flexural Strength: Tensile Strength, per ASTM C 348, at 28 days: 1260 psi (8.7 MPa) |
| | | | Tensile Strength, per ASTM C 190, at 28 days: 720 psi (5 MPa) |
| | | | Maxxon Level-Right PLUS |
| | | | Material: Polymer modified hydraulic cement |
| | | | Dry Density: Approximately 120-125 pcf (1922 - 2003 kg/m3) |
| | | | Compressive Strength, per modified ASTM C 109, at 28 days: 5500 - 7000 psi (38-48 MPa) |
| | | | Flexural Strength: Tensile Strength, per ASTM C 348, at 28 days: 1250 psi (8.6 MPa) |
| | | | Tensile Strength, per ASTM C 190, at 28 days: 810 psi (6 MPa) |
| | | | Maxxon Level-Right FS-10 |
| | | | Material: Polymer modified hydraulic cement. |
| | | | Dry Density: Approximately 120-125 pcf (1922 - 2003 kg/m3) |
| | | | Compressive Strength, per modified ASTM C 109, at 28 days: 5500 - 7200 psi (38-50 MPa) |
| | | | Tensile Strength, per ASTM C 190, at 28 days: 1200 psi (8.3 MPa) |