 | | | Waterproof Sealer: Clear, non-staining, waterborne acrylic-base penetrating sealerprimer containing |
| | | low quantities of VOCs (volatile organic compounds); SEAL-KRETE Waterproofing Sealer. |
| | | | Resistance to Water Penetration: Minimum rating of Excellent, when tested according to |
| | | | FS TT-P-0035, modified using 4 by 8 by 16 inch (100 by 200 by 400 mm) concrete block, |
| | | | at equivalent of 98 mph (158 km/h) wind speed |
| | | | Water Vapor Transmission: 3.6 perms (207 ng/(Pa s sqm), maximum, when tested |
| | | | in accordance with ASTM D 1653. |
| | | | Corrosion Resistance: No visible degradation of film after 48 hours, when subjected to |
| | | | sodium hypochlorite, hydrochloric acid, sodium chloride (salt), and chlorine. |
| | | | Solids Content: 25 percent, minimum. |
| | | | Flammability: Non-flammable. |
| | | | Toxicity: USDA approved for application to surfaces where there is possibility of contact with food. |
| | | | Tensile Strength: 1000 psi (6890 kPa). |
| | | | Freeze/Thaw Stability: Stable. |
| | | | Fading Resistance: Approximately 0.05 percent, maximum, after 312 hours of testing. |
| | | | Comply with Florida Department of Transportation Specification 926-16 for Type 'O' Compounds, |
| | | | Florida DOT Method FM5-518. |
| | | | Pigmenting Agent: |
| | | Heavy Duty Commercial Grade Waterproofer: Advanced, high-solids, siliconized, acrylic blend designed to protect and strengthen bare, |
| | | porous concrete and masonry, such as split-face or fluted concrete block. |
| | | | Resistance to Water Penetration: No more than 25 percent dampness appearing on back of wall specimen, |
| | | | when tested in accordance with ASTM E 514 for 4 hours. |
| | | | Solids Content: 25 percent minimum. |
| | | | Meets FS SS-W-110C for Water Repellency on Masonry. |
| | | | Mildew Resistance: ASTM D 5590. |
| | | | Flammability: Non-flammable. |
| | | | Toxicity: USDA approved for application to surfaces where there is possibility of contact with food. |